High Quality Fiberglass Woven Roving - Fiberglass Woven Roving – Beihai Fiberglass
High Quality Fiberglass Woven Roving - Fiberglass Woven Roving – Beihai Fiberglass Detail:
E-Glass Woven Rovings are bidirectional fabric made by interweaving direct rovings.
F-E-Glass Woven Rovings are compatible with many resin systems, such as unsaturated polyester, vinyl ester, epoxy and phenolic resins.
E-Glass Woven Roving is a high-performance reinforcement widely used in hand lay up and robot processes for the production of boats, vessels, plane and automotive parts, furniture and sports facilities.
| Product Features： | |
| 1.Warp and weft rovings aligned in a parallel and flat manner, resulting in uniform tension. 2.Densely aligned fibers, resulting in high dimensional stability and making handling easy. 3.Good mold ability, fast and complete wet in resins, resulting in high productivity. 4.Good transparency and high strength of composite products. |
 |
Product Specifications:
|
Property |
Area Weight |
Moisture Content |
Size Content |
Width |
|
（%） |
（%） |
（%） |
（mm） |
|
|
Test Method |
IS03374 |
ISO3344 |
ISO1887 |
|
|
EWR200 |
±7.5 |
≤0.15 |
0.4-0.8 |
20-3000 |
|
EWR260 |
||||
|
EWR300 |
||||
|
EWR360 |
||||
|
EWR400 |
||||
|
EWR500 |
||||
|
EWR600 |
||||
|
EWR800 |
Product List:
|
Items |
Warp Tex |
Weft Tex |
Warp Density Ends/cm |
Weft Density Ends/cm |
Areal Weight g/m2 |
Combustible Content(%) |
| WRE100 | 300 | 300 | 23 | 23 | 95-105 | 0.4-0.8 |
| WRE260 | 600 | 600 | 22 | 22 | 251-277 | 0.4-0.8 |
| WRE300 | 600 | 600 | 32 | 18 | 296-328 | 0.4-0.8 |
| WRE360 | 600 | 900 | 32 | 18 | 336-372 | 0.4-0.8 |
| WRE400 | 600 | 600 | 32 | 38 | 400-440 | 0.4-0.8 |
| WRE500 | 1200 | 1200 | 22 | 20 | 475-525 | 0.4-0.8 |
| WRE600 | 2200 | 1200 | 20 | 16 | 600-664 | 0.4-0.8 |
| WRE800 | 1200*2 | 1200*2 | 20 | 15 | 800-880 | 0.4-0.8 |
● Special specification can be produce according to customer requirements.
Packaging:
Each woven roving is wound onto a paper tube which has an inside diameter of 76mm and the mat roll has a diameter of 220mm. The woven roving roll is wrapped up with plastic film，and then packed in a cardboard box or wrapped up with kraft paper. The rolls can be horizontally placed. For transportation, the rolls can be loaded into a cantainer directly or on pallets.
Storage:
Unless otherwise specified,It should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15℃～35℃ and 35%～65% respectively.
Trade Terms
MOQ: 20000kg/20’FCL
Delivery: 20 days after deposit receipt
Payment: T/T
Packing:40kgs/roll, 1000kgs/pallet.
Product detail pictures:
Related Product Guide:
To be a result of ours specialty and service consciousness, our company has won a superb reputation between customers all around the environment for High Quality Fiberglass Woven Roving - Fiberglass Woven Roving – Beihai Fiberglass , The product will supply to all over the world, such as: Madagascar, Honduras, Mexico, So that you can utilize the resource from the expanding info in international trade, we welcome shoppers from everywhere on-line and offline. In spite of the good quality solutions we offer, effective and satisfying consultation service is supplied by our specialist after-sale service team. Product lists and detailed parameters and any other info weil be sent to you timely for your inquiries. So please make contact with us by sending us emails or call us if you have any questions about our corporation. ou may also get our address info from our web page and come to our company to get a field survey of our merchandise. We are confident that we are going to share mutual achievement and create strong co-operation relations with our companions in this marketplace. We're searching forward for your inquiries.
By Stephanie from Albania - 2017.10.13 10:47
This company has the idea of "better quality, lower processing costs, prices are more reasonable", so they have competitive product quality and price, that's the main reason we chose to cooperate.
By Belle from Morocco - 2017.09.09 10:18